Semi-conductive Screen Compound

Home » Products » Cable Compounds » Semi-conductive Screen Compound
inquiry form

Polymer, usually behaves as insulator, should be added much carbon black to become semi-conductive. However, the chemical and physical properties and processing performances may decrease in the process. Our company employs high electrical-conductivity carbon black to solve the problem. Our product features smooth surface, without any burrs. Besides, it has an appropriate degree of crosslinking and good rheological and electrical prosperity. Heat, copper and cross resistance are available as well. It is applicable to insulation shield for crosslinked polyethylene cable that used under 35kv.

Parameters

Peroxide crosslinkable Grade Density (g/cm3) Tensile strength (Mpa) Elongation at break (%) Volume Resistivity at 20℃ (Ω·cm) Stripping Force (N/cm)
S R - 0 611-10 / 3 5 1.1 16 280 60 /
SR - 0 612-10/ 35 1.16 16 250 60 29
SR - 0 613 1.14 16 270 60 /
Peroxide crosslinkable thermoplastic Grade Density (g/cm3) Tensile strength (Mpa) Elongation at break (%) Volume Resistivity at 20℃ (Ω·cm) Stripping Force (N/cm)
SR- 0610 1.1 12 210 20 /

As an experienced semi-conductive screen compound manufacturer and supplier in China, Surrey also provides rodent/ termite resistant cable compound, fiber for fishing line (10D-300D), general bulletproof vest, UD prepreg, and more.